Aluminum Alsi0.9mgmn and Aluminum Alloy Alsi0.9mgmn Sheet or Plate

Model NO.
A96081/AlSi0.9MgMn
Surface Treatment
Mill Finish
Alloy
Alloy
Temper-1
6065-T6/T62
Melting Point
600-650
Density
2.7-2.8g/cm3
Standard
ASTM B210 ASTM B221 ASTM B241 ASTM B345 ASTM B361
Application-1
Frame Work, Brackets, Interior & Exterior Architec
Form
Sheet,Plate,Bar,Rod,Tube,Pipe,Strip,Foil an
Transport Package
Standard Export Packaging
Specification
0.5-200mm*500-2500mm*500-100000mm
Trademark
Taixie
Origin
China
HS Code
7606910000
Production Capacity
10 Tons Per Month
Reference Price
$ 17.10 - 26.10
Contact Us

Product Description

[aluminium  alloy 6081-T6/AlSi0.9MgMn] 
Introduction:

6070 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. 6070 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6070. A96070 is the UNS number.

It originally received its standard designation in 1962.

The properties of 6070 aluminum include two common variations. This page shows summary ranges across both of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare 6070 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.


[aluminium  alloy 6081-T6/AlSi0.9MgMn] 
Application:

is used in manufacturing pipelines and heavy duty welded structures.


[aluminium  alloy 6081-T6/AlSi0.9MgMn] 
Chemistry:

Chemical Composition

The chemical composition of aluminium / aluminum 6070 alloy is outlined in the following table.

ElementContent (%)
Aluminium / aluminum, Al97
Silicon, Si1.40
Magnesium, Mg0.80
Manganese, Mn0.70
Copper, Cu0.28

Physical Properties

The physical properties of aluminium / aluminum 6070 alloy are tabulated below.

PropertiesMetricImperial
Density2.6-2.8 g/cm30.0939- 0.101 lb/in3

Mechanical Properties

The mechanical properties of aluminium / aluminum 6070 alloy are outlined in the following table.

PropertiesMetricImperial
Tensile strength145 MPa21031 psi
Yield strength69 MPa10008 psi
Shear strength97 MPa14069 psi
Fatigue strength62 MPa8993 psi
Elastic modulus70-80 GPa10153-11603 ksi
Poisson's ratio0.330.33
Elongation20%20%
Hardness3535

Thermal Properties

The thermal properties of the aluminium / aluminum 6070 alloy are given in the following table.

PropertiesConditions
TempTreatment
Thermal conductivity175 W/mK25ºC/77ºFT6
 
ElementWeight %
Al 96.8 
Si 1.40 
Cu 0.28 
Mn 0.7 
Mg 0.80 
 
Properties Conditions 
T (°C)Treatment
Density (×1000 kg/m3)2.6-2.825 
Poisson's Ratio0.3325 
Elastic Modulus (GPa)70-8025 
Tensile Strength (Mpa)145 25 O  more
Yield Strength (Mpa)69 
Elongation (%)20 
Reduction in Area (%) 
Hardness (HB500)35 25 O more
Shear Strength (MPa)97 25 O  more
Fatigue Strength (MPa)62 25 O  more
 
Properties Conditions 
T (°C)Treatment
Thermal Conductivity (W/m-K)172 25 T6 
 
 
Properties Conditions 
T (°C)Treatment
Electric Resistivity (10-9W-m)39 25 T6 


[aluminium  alloy 6081-T6/AlSi0.9MgMn] 
Surface 

mill finish ,  not polished,
brushed
mirror 
embossed 
oxidized
cold-rolled
hot-rolled

[aluminium  alloy  6081-T6/AlSi0.9MgMn]
Specification:

Shape/Form : sheet,plate,bar,rod,tube,pipe,strip,foil and so on 

Surface : Mill Finish(Not Polished ) ,polished  ,colour-coated, sand blasting  , brushed,mirror ,embossed ,oxidized,anodic oxidation    cold-rolled,hot-rolled  


This  is our  warehouse :Aluminum Alsi0.9mgmn and Aluminum Alloy Alsi0.9mgmn Sheet or Plate


Aluminum Alsi0.9mgmn and Aluminum Alloy Alsi0.9mgmn Sheet or Plate



Aluminum Alsi0.9mgmn and Aluminum Alloy Alsi0.9mgmn Sheet or Plate




This  is packaging :

Aluminum Alsi0.9mgmn and Aluminum Alloy Alsi0.9mgmn Sheet or Plate


Aluminum Alsi0.9mgmn and Aluminum Alloy Alsi0.9mgmn Sheet or Plate
 

 

Aluminum Sheet

COMICGENESIS.COM, 2023